Pb(Zr0.52Ti0.48)O3 (PZT) thin film on Pt/RuO2 double electrode was successfully prepared by using a new alkoxide-alkanolamine, sol-gel method. It was observed that the use of Pt/RuO2 double electrode reduced leakage current, resulting in a marked improvement in the leakage characteristics and more reliable capacitors. Typical P-E hysteresis behavior was observed even at low applied voltage of 5 V, manifesting greatly improved remanence and coercivity. Fatigue and breakdown characteristics, measured at 5 V, showed stable behavior, and no degradation in polarization was observed up to 1011 cycles.